Effect of Cu Content on Corrosion Behavior of 7xxx Series Aluminum Alloys

Please use this identifier to cite or link to this item: http://hdl.handle.net/1811/45410

Show full item record

Files Size Format View
FrankelG_Journa ... y_2004_v151n5_pB271-83.pdf 1.688Mb PDF View/Open

Title: Effect of Cu Content on Corrosion Behavior of 7xxx Series Aluminum Alloys
Creators: Meng, Qingjiang; Frankel, G. S.
Keywords: electrochemical impedance spectroscopy (EIS)
breakdown potential
Cu content
7xxx aluminum alloys
Issue Date: 2004
Citation: Meng, Qingjiang; Frankel, G. S. "Effect of Cu Content on Corrosion Behavior of 7xxx Series Aluminum Alloys," Journal of the Electrochemical Society, v. 151, no. 5, 2004, pp. B271-B283.
Abstract: The corrosion behavior of 7xxx aluminum alloys with various Cu content was investigated using polarization and electrochemical impedance spectroscopy (EIS) techniques. Two breakdown potentials were found in Cu-containing alloys in deaerated chloride solution, and the values increased logarithmically with increasing Cu content. However, in aerated chloride solution, polarization resistance as determined by EIS decreased with increasing Cu content. The first breakdown potential corresponded to transient dissolution associated with attack of the fine hardening particles and the surrounding solid solution in a thin surface layer. The second breakdown potential was associated with combined intergranular and selective grain attack. The correlation between the microstructure, especially Cu content, and corrosion behavior was made by composition analysis of the grain boundary regions including precipitate free zone and grain boundary precipitates as well as the matrix by scanning transmission electron microscopy. The corrosion potential increased with increasing alloy Cu content in aerated chloride solutions because of enhanced rates of oxygen reduction. This degraded the corrosion resistance despite the increase in the breakdown potentials with Cu content.
URI: http://hdl.handle.net/1811/45410
ISSN: 0013-4651 (print)
Bookmark and Share
Attribution-ShareAlike 3.0 Unported This item is licensed under a Creative Commons License:
Attribution-ShareAlike 3.0 Unported